Rate and higher active ingredient content compared with PCE 50% . According to the temperature conditions and technical requirements of the project, adopting a prototype or composite measures, Polycarboxylate Superplasticizer can be used to formulate various types of high strength concrete below C80. High adaptability to cement, and it can meet the technical requirements of all types of concrete throughout the year while taking appropriate measures
Conforming to standard of SS EN 934and ASTM C 494
Main Use & Advantages
Application amount of 0.2%-0.6% most effective high range water reducing in the market which the reducing rate can go up to 35-40%. Because of their Low chloride and alkali content, no corrosion to steel-bar, high stability & environmental friendly and nontoxic characters, they have been warm welcomed in high strength concrete for railway, haven, traffic, bridge and electric power., got good feedback from worldwide customers. It is excellent superplasticizer in premix of construction and cast-in-place concrete.
– High water reducing ratio: Excellent dispersity and water reducing ratio can reach 36% or above at saturated addition amount
– Environmental friendly products: No pollution during production.
– Low-consume, Low-cost: It can be produced in little cycle and little-consume. So it having low-cost. Especially it can be used in commercial concrete
Na2SO4 Content %
Chloride Content %
Alkali Content %
Cement Paste Fluidity
Concrete Water Reduction Ratio
Concrete Air Content
Ratio Of Bleeding Rate
1H Slump Retention
Packing ,Storage and Transportation
1.Steel Drum 250kg or IBC tank as well as Flexi Tank or plastic drum available.
2.The liquid is filled with plastic bucket or iron bucket, and the barrel is sealed to prevent liquid spilling or evaporation drying. Other forms of packing can be decided by the two sides.
3.This product shall be transported according to the standard of common chemical products.